Versollan™ RU 2204X Datasheet,TPE,PolyOne Corporation-SHANGHAI SUSHENG

Message
Versollan™RU 2204X is the first product of a new generation of high-performance polyurethane (TPU) alloys that can be molded by injection molding. It can produce a rubber-like feel and appearance and shorten the cycle period, while having the performance of TPU. New Products. Commercial norms have not yet been established. can bond with PC, ABS, PC/ABS and copolyester Good wear resistance Short preparation time during processing Good chemical and oil resistance Matte surface Similar to rubber, soft to the touch

General Information
Features	Good wear resistance Good chemical resistance Oil resistance
Appearance	Natural color
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.14	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR)			ASTM D1238
190°C/2.16 kg	11	g/10 min	ASTM D1238
200°C/5.0 kg	76	g/10 min	ASTM D1238
Molding Shrinkage - Flow	1.2 - 1.6	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	55		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ASTM D412
100% strain, 23°C ²	1.86	MPa	ASTM D412
300% strain, 23°C ³	3.03	MPa	ASTM D412
Tensile Strength (Break, 23°C)	12.4	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	690	%	ASTM D412
Tear Strength	42.0	kN/m	ASTM D624
Compression Set (23°C, 22 hr)	26	%	ASTM D395B

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity			ASTM D3835
200°C, 1340 sec^-1	69.0	Pa·s	ASTM D3835
200°C, 11200 sec^-1	13.9	Pa·s	ASTM D3835

Injection	Nominal Value	Unit
Drying Temperature	48.9 - 54.4	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	< 0.030	%
Suggested Max Regrind	20	%
Rear Temperature	163 - 188	°C
Middle Temperature	182 - 193	°C
Front Temperature	188 - 210	°C
Nozzle Temperature	193 - 216	°C
Processing (Melt) Temp	188 - 210	°C
Mold Temperature	21.1 - 32.2	°C
Back Pressure	0.00 - 0.552	MPa
Screw Speed	75 - 125	rpm

Injection instructions
Color concentrates with polyether or polyester-based urethane carriers are most suitable for coloring Versollan™ RU 2204X. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on hardness. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Polypropylene (PP) based color concentrates are not recommended because they significantly affect adhesion of the TPE to the substrate. Concentrates based on TPE should not be used. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versollan™ RU 2204X with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versollan™ RU 2204X should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 300 to 700 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 4 to 10 secHold Time (Thin Part): 1 to 3 sec

Injection instructions

Color concentrates with polyether or polyester-based urethane carriers are most suitable for coloring Versollan™ RU 2204X. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on hardness. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Polypropylene (PP) based color concentrates are not recommended because they significantly affect adhesion of the TPE to the substrate. Concentrates based on TPE should not be used. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versollan™ RU 2204X with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versollan™ RU 2204X should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 300 to 700 psi2nd Stage - Hold Pressure: 30% of BoostHold Time (Thick Part): 4 to 10 secHold Time (Thin Part): 1 to 3 sec

Note Message
1 .	2 hours
2 .	Mouth die c
3 .	C mould

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versollan™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wVYMPg_Versollan-RU-2204X.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
VITAMIDE® AD38BK6319	Jackdaw Polymers	Nylon 66	VITAMIDE®
DURANEX® 531HS	Polyplastics Co., Ltd.	PBT	DURANEX®
Magnobond 6021-1	Magnolia Plastics, Inc.	Epoxy	Magnobond
ALCUDIA® LDPE CN-105	REPSOL	LDPE	ALCUDIA® LDPE
WELLAMID Nylon 6000 GV 40 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 6	WELLAMID Nylon