Adflex Z 108 S
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wUq6av_Adflex-Z-108-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex Z 108 S is a reactor TPO (thermoplastic polyolefin) manufactured using the LyondellBasell's proprietary Catalloy process technology. Adflex Z 108 S features a very high softness, a very low flexural modulus and a high melt flow rate. It is used for injection molding, impact modification, extrusion coating, soft compounding, film and fiber applications. It is also ideal for the modification of polypropylene homopolymer and random copolymer without altering the transparency. The grade is available in natural pellet form. For regulatory compliance information see Adflex Z 108 S Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, 15 sec | 85 | ||
| Shore D, 15 sec | 30 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 5.00 | MPa | |
| Break | 6.00 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 20 | % | |
| Break | > 800 | % | |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 1 | 62.0 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.0 | kJ/m² | |
| 23°C | No Break | ||
| Instrumented Dart Impact 2 | ASTM D3763 | ||
| -40°C, 3.20 mm, Energy at Peak Load, Ductile Failure | 18.0 | J | |
| 23°C, 3.20 mm, Energy at Peak Load, Ductile Failure | 10.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 37.0 | °C | ISO 75-2/B |
| Ductile / Brittle Transition Temperature | -55.0 | °C | ISO 6603-2 |
| Vicat Softening Temperature | 53.0 | °C | ISO 306/A50 |
| Melting Temperature | 142 | °C | ISO 11357-3 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°, 3200 µm, Injection Molded) | 66 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | Die C, 50 mm/min |
| 2 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam RF0077E | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Sylvin 7833-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vital-Line SHM3600G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Ultradur® B 4441 G5 | BASF Corporation | PBT | Ultradur® |
| ENFLEX S3190A | ENPLAST Americas, a Ravago Group Company | TPE | ENFLEX |