Luran® S KR2858G3
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Styrolution |
| Trademark: | Luran® S |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wUTg0R_Luran-S-KR2858G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran S KR2858G3 is a 15% glass fiber reinforced grade offering enhanced heat resistance and superior rigidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.4 | % | |
| Equilibrium, 23°C, 50% RH | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 2.5 | % | |
| Break, 23°C | 2.5 | % | |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 115 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 120 | °C | ISO 306/A50 |
| -- | 115 | °C | ISO 306/B50 |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y600 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Sylvin 8303-60 Black | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| CERTENE™ LLHR-538U | Muehlstein | MDPE | CERTENE™ |
| DIOSHY® AB-885EM | DIOSHY Co.,Ltd. | SEBS | DIOSHY® |
| LubriOne™ PS-30CF/15T BK701 | PolyOne Corporation | PBT | LubriOne™ |