Sunny® PET EN130
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wT4KkP_Sunny-PET-EN130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP reinforced polybutylene terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.54 | g/cm³ | ASTM D792 |
| 23°C | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 to 0.60 | % | ASTM D955 |
| 23°C | 0.30 to 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.10 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 170 | MPa | ASTM D638 |
| -- | 170 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 9500 | MPa | ASTM D790 |
| 50.0 mm Span | 9800 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 203 | MPa | ASTM D790 |
| -- 4 | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 220 | °C | ASTM D648, ISO 75-2/Af |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 250 | °C | |
| Front Temperature | 245 | °C | |
| Processing (Melt) Temp | 255 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 V25 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| VITAMIDE® AR36GY6581 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| APEL™ APL8008T | Mitsui Chemicals America, Inc. | COC | APEL™ |
| Chemraz 534 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| DURANEX® HN7330N/B | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |