| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | HIFOR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wRbpoW_HIFORLT74151.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WESTLAKE HIFOR Polyethylene LT74151 is a high strength linear low density polyethylene containing high slip and high antiblock. It is designed for blown film applications and is well suited for consumer and industrial packaging markets which require impact and tear strength. Films produced using LT74151 exhibit low imperfections and facilitate production at thinner gauges. Application/Uses
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 221 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 241 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 50.3 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 39.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 750 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1000 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 170 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 30 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 35 | % | ASTM D1003 |
| Additional Information |
|---|
| Gauge of test specimens 1.0 mil fabricated on a 6" die, 2.5" 24:1 L:D barrier screw, 2.4:1 BUR, 100-mil die gap, 15" frostline height, 450° F melt temperature, and 7.5 lb/hr/inch die output. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STABAMID® 27 FE 5 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| TRIPET® 2500G40 | Samyang Corporation | PET | TRIPET® |
| Beamset 1461 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| Chemlon® 60GS6 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Karina STRAW PVC COMPOUND 800-38/ 14-F-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |