INSULCAST® 502/INSULCURE 9
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wR6B7g_INSULCAST-502-INSULCURE-9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSULCAST 502 is an unfilled epoxy with low viscosity for general purpose casting and impregnation, exhibiting excellent electrical and physical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 73.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.4 | % | ASTM D638 |
| Flexural Strength | 121 | MPa | ASTM D790 |
| Compressive Strength | 96.5 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 7.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.23 | W/m/K | |
| Heat Deflection Temperature | 85 | °C | |
| Service Temperature | 105 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.00 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 0.023 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 13 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Shelf Life (25°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 1 | Amber | ||
| -- 2 | Clear/Transparent | ||
| Density | |||
| -- 3 | 0.968 | g/cm³ | |
| -- 4 | 1.13 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| 25°C 5 | 0.055 | Pa·s | |
| 25°C 6 | 0.20 | Pa·s | |
| 25°C 7 | 0.70 | Pa·s | |
| Curing Time (25°C) | 4.0 to 8.0 | hr | |
| Pot Life 8(25°C) | 30 | min |
| Note Message | |
|---|---|
| 1 . | INSULCURE 9 |
| 2 . | INSULCAST 502 |
| 3 . | INSULCURE 9 |
| 4 . | INSULCAST 502 |
| 5 . | INSULCURE 9 |
| 6 . | Mixed |
| 7 . | INSULCAST 502 |
| 8 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell ACP 6541A | LyondellBasell Industries | HDPE | Purell |
| Badamid® A70 H | Bada AG | Nylon 66 | Badamid® |
| Karina RED PVC COMPOUND 850-42/207-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PENTAMID A GV20 GK10 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| LEXAN™ HFD4472 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |