KEPEX 3300SA is an unfilled, impact modified, and hight melt flow PBT. It exhibits good toughness and impact strength. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.8 to 2.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 30 | % | ASTM D638 |
| Flexural Modulus (23°C) | 2350 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 150 | °C | |
| 1.8 MPa, Unannealed | 50.0 | °C | |
| Melting Temperature | 220 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 230 to 250 | °C | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Promyde® B30 P2 G30 | NUREL, S.A. | Nylon 6 | Promyde® |
| Latilub 80-15T G/30 | LATI S.p.A. | PPS | Latilub |
| Petro Rabigh PP AZ564G | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| Petrothene® L2560S | LyondellBasell Industries | LDPE | Petrothene® |
| KMI PP KM-058IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |