QR Resin QR-1000-GF30
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wQzewL_QR-Resin-QR-1000-GF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available with UV (V) or Release (R). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 to 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 131 | MPa | ASTM D638 |
| Flexural Modulus | 6890 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Drying Time, Maximum | 6.0 | hr | |
| Rear Temperature | 282 to 304 | °C | |
| Middle Temperature | 293 to 316 | °C | |
| Front Temperature | 304 to 338 | °C | |
| Nozzle Temperature | 304 to 338 | °C | |
| Processing (Melt) Temp | 316 to 343 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| North American Santicizer® 278 | Ferro Corporation | Plasticizer | North |
| Karina IVORY PVC COMP. -E 850-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PALFORM® R C 09 | pal plast GmbH | Acetal (POM) Copolymer | PALFORM® |
| EcoHumer BFX3091 | WooSung Chemical Co., Ltd. | PBAT | EcoHumer |
| NILAMID® XS1 GF60 | Nilit Plastics | Nylon, Unspecified | NILAMID® |