Sasol Polymers PP HLR102

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Sasol Polymers
Trademark:	Sasol Polymers PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wPIVwU_Sasol-Polymers-PP-HLR102.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Features

Medium flow

Low water carry over during the extrusion process

Particularly suitable for processing on high speed tape extrusion lines

Applications
Extrusion

Production of raffia tapes as used in the manufacture of woven fabric

Block-bottom cement bags

Sacks and bags

Flexible intermediate bulk containers (FIBC's)

Injection moulding

Domestic, industrial and general purpose articles

General Information
Additive	Processing stabilizer
Features	Homopolymer Good processing stability Medium liquidity Compliance of Food Exposure Low water portability
Uses	Strap Bags Industrial application Household goods Container General
Agency Ratings	EC 1935/2004 FDA 21 CFR 177.1520(a)(3)(i)(c)(1) FDA 21 CFR 177.1520(c) 3.1a
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	5.3	g/10 min	ISO 1133
Molding Shrinkage			ISO 294-4
Vertical flow direction	1.4	%	ISO 294-4
Flow direction	1.5	%	ISO 294-4

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	72.0	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1550	MPa	ISO 527-2/1A/1
Tensile Stress (Yield)	34.0	MPa	ISO 527-2/1A/50
Tensile Strain			ISO 527-2/1A/50
Yield	9.0	%	ISO 527-2/1A/50
Fracture	> 50	%	ISO 527-2/1A/50
Flexural Modulus	1500	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	3.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	85.0	°C	ISO 75-2/B
1.8 MPa, not annealed	53.0	°C	ISO 75-2/A
Vicat Softening Temperature
--	154	°C	ISO 306/A120
--	90.0	°C	ISO 306/B120
Melting Temperature	163	°C	ISO 11357-3

Injection	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Rear Temperature	180 - 260	°C
Middle Temperature	220 - 280	°C
Front Temperature	240 - 280	°C
Nozzle Temperature	220 - 280	°C
Processing (Melt) Temp	220 - 280	°C
Mold Temperature	20.0 - 60.0	°C

Injection instructions
Zone 4: 240 to 280°C

Extrusion	Nominal Value	Unit
Hopper Temperature	40.0 - 60.0	°C
Cylinder Zone 1 Temp.	220 - 280	°C
Cylinder Zone 2 Temp.	240 - 280	°C
Cylinder Zone 3 Temp.	240 - 280	°C
Cylinder Zone 4 Temp.	240 - 280	°C
Cylinder Zone 5 Temp.	240 - 280	°C
Melt Temperature	220 - 280	°C
Die Temperature	240 - 260	°C

Resin Grade	Manufacturer	Category	Trademark
APEX® 1565	Teknor Apex Company	PVC, Flexible	APEX®
Ferro PP TPP30AE85HB TAN	Ferro Corporation	PP Homopolymer	Ferro PP
LNP™ THERMOCOMP™ KF008 compound	SABIC Innovative Plastics Europe	Acetal (POM) Copolymer	LNP™ THERMOCOMP™
POLYCASA® ACRYL G 88 E	Polycasa	Acrylic (PMMA)	POLYCASA® ACRYL
Durethan® AKV 35 H2.0 901510	LANXESS GmbH	Nylon 66	Durethan®