EMERGE™ PC/PET 9500CR
| Category: | PC+PET , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wNdx2Z_EMERGE-PC-PET-9500CR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC/PET 9500CR Advanced Resin is a polycarbonate blend with excellent chemical and ignition resistance properties. This grade was designed for use in medical equipment housings and other applications that are subject to repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. It has a UL 94 rating of V0 at 2.0 mm. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 260°C/5.0 kg | 10 | g/10 min | |
| 265°C/5.0 kg | 13 | g/10 min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.60 to 0.95 | % | |
| Across Flow | 0.50 to 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm, Injection Molded) | 2330 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 53.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 45.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 4.1 | % | |
| Break, 3.20 mm, Injection Molded | 150 | % | |
| Flexural Modulus 4(3.20 mm, Injection Molded) | 2270 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm, Injection Molded) | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 750 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| 0°C, 3.20 mm, Injection Molded, Peak Energy | 49.0 | J | |
| 0°C, 3.20 mm, Injection Molded, Total Energy | 62.0 | J | |
| 23°C, 3.20 mm, Injection Molded, Peak Energy | 45.0 | J | |
| 23°C, 3.20 mm, Injection Molded, Total Energy | 60.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 109 | °C | |
| 1.8 MPa, Unannealed | 79.0 | °C | |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 6 |
| CLTE - Flow (-40 to 80°C) | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.2E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| 1.60 mm, in Oil | 31 | kV/mm | |
| 3.20 mm, in Oil | 18 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.28 | ||
| 1 MHz | 3.12 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.020 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm 7 | V-1 | ||
| 2.00 mm 8 | V-0 | ||
| 2.50 mm 9 | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 825 | °C | |
| 2.00 mm | 960 | °C | |
| 2.50 mm | 960 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 249 to 282 | °C | |
| Mold Temperature | 43.3 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 8 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 9 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-315 | Teknor Apex Company | TPE | Medalist® |
| VESTAMID® L L-GF15 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Ateva® 2810A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Fluoroelastomer 931 | Greene, Tweed & Co. | Fluorelastomer | Fluoroelastomer |
| Huaxia Shenzhou FKM 246V | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |