Badamid® PA12 GM/GR40 H
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wMI3qV_Badamid-PA12-GM-GR40-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA12 injection moulding grade with 40% milled glass fibres and graphite reinforcement; Grade with high wear resistance and low surface friction for tribological applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 5100 | MPa | ISO 3167-A |
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break (23°C) | 11 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 60 | kJ/m² | |
| 23°C | 70 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 170 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 2 | 178 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 mm/min |
| 2 . | 10 K/Min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silplus® 60 EX | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| Cellophane™ OptiTwist™ | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| FLEXITEQ™ F55A110 | Marplex Australia Pty. Ltd. | TPV | FLEXITEQ™ |
| Echo® RPH20TC BK | Ravago Manufacturing Americas, LLC | PP Homopolymer | Echo® |
| LUVOCOM® TPU-7682 | Lehmann & Voss & Co. | PUR, Unspecified | LUVOCOM® |