| 4DUR 9K22720 is a Standard Flow Carbon Fibre Reinforced PBT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 800 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 16000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 120 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | ISO 180/1U |
| 23°C | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 2 | 225 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3653T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| REPOL® H350FG | Reliance Industries Limited | PP Homopolymer | REPOL® |
| YUNGSOX® PP 1040U | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| CONTINUUM™ DGDA-2492N NT | The Dow Chemical Company | HDPE | CONTINUUM™ |
| LNP™ LUBRICOMP™ QAP22S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |