LNP™ THERMOCOMP™ LC00APXQ compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wLSpRD_LNP-THERMOCOMP-LC00APXQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LC00APXQ is a compound based on Polyetheretherketone resin containing 50% Carbon Fiber. Added features of this material include: Exceptional Processing, Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound LC00APXQ Product reorder name: LC00APXQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.13 to 0.25 | % | |
| Across Flow : 24 hr | 0.60 to 1.3 | % | |
| Water Absorption (24 hr, 50% RH) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 49800 | MPa | ASTM D638 |
| -- | 47400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 328 | MPa | ASTM D638 |
| Break | 320 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.2 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 40500 | MPa | ASTM D790 |
| -- 5 | 40700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 473 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 505 | MPa | ASTM D790 |
| Shear Modulus | 5190 | MPa | ASTM C273 |
| Shear Strength | 114 | MPa | ASTM C273 |
| Poisson's Ratio | 0.45 | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 77 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 770 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 7.50 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 335 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 150°C | 2.0E-6 | cm/cm/°C | |
| Transverse : -40 to 150°C | 2.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-3260-1 | Teknor Apex Company | TPE | Telcar® |
| DOW™ HDPE DGDB-2480 NT | The Dow Chemical Company | HDPE | DOW™ HDPE |
| NEXUS Reprocessed TPO 12/55D RBK | Nexus Resin Group, LLC. | TPO (POE) | NEXUS Reprocessed |
| BONDYRAM® 1004 | Polyram Ram-On Industries | PP Homopolymer | BONDYRAM® |
| Evoprene™ 3274 | AlphaGary | SBS | Evoprene™ |