INLUBE INX-SAN-09055
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INLUBE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wL4HqE_INLUBE-INX-SAN-09055.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAN COMPOUND WITH GRAPHITE, GLASS BEADS AND PTFE. DESIGNED FOR OPTIMUM DIMENSIONAL STABILITY AND WEAR RESISTANCE IN AQUEOUS ENVIRNMENTS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.20 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.060 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus | 6.21 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact | 160 to 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 82.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alpha PVC 3006R-90 CLEAR 000X | AlphaGary | PVC, Flexible | Alpha PVC |
| AMTOPP TL15 | Inteplast Group | PP, Unspecified | AMTOPP |
| EPO-TEK® B9021-15 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| KOCETAL® WR301LOBK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| TOTAL Polystyrene Impact 4440H | TOTAL Refining & Chemicals | PS (HIPS) | TOTAL Polystyrene |