Celanex® 3316
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wHqxre_Celanex-3316.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3316 is a non-exuding flame retarded (UL and CSA approved V-0 at 1/32 inch and 5V at 1/16 inch), 30% fiberglass reinforced polybutylene terephthalate which has an excellent balance of mechanical properties and processability. It is well suited for electrical connector applications where its UL approved 50% regrind use capability allows maximum use of purchased product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.30 - 0.50 | % | ASTM D955 |
| Vertical flow direction | 0.80 - 1.3 | % | ISO 294-4 |
| Flow direction | 0.10 - 0.80 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.16 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 89 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 9650 | MPa | ASTM D638 |
| -- | 10700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Fracture, 23°C | 134 | MPa | ASTM D638 |
| Fracture | 135 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Fracture, 23°C | 2.5 | % | ASTM D638 |
| Fracture | 2.5 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 10300 | MPa | ISO 178 |
| Flexural Stress (23°C) | 200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 8.5 | kJ/m² | ISO 179/1eA |
| 23°C | 8.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 42 | kJ/m² | ISO 179/1eU |
| 23°C | 59 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 7.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 0.45 MPa, annealed | 221 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 206 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 208 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 165 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 225 | °C | ISO 306/B50 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3, ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 2.0E+16 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 2 | 20 | kV/mm | ASTM D149 |
| -- | 34 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 1 MHz | 3.50 | ASTM D150 | |
| 100 Hz | 3.60 | IEC 60250 | |
| 1 MHz | 2.90 | IEC 60250 | |
| Dissipation Factor | |||
| 1 MHz | 0.020 | ASTM D150 | |
| 100 Hz | 3.3E-3 | IEC 60250 | |
| 1 MHz | 0.015 | IEC 60250 | |
| Arc Resistance | 106 | sec | ASTM D495 |
| Comparative Tracking Index | 250 | V | IEC 60112, ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-0 | UL 94 | |
| 1.50 mm | 5VA | UL 94 | |
| Oxygen Index | 30 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 50 | % | |
| Hopper Temperature | 20.0 - 50.0 | °C | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 235 - 250 | °C | |
| Nozzle Temperature | 250 - 255 | °C | |
| Processing (Melt) Temp | 235 - 255 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 250 to 260°CZone 4 Temperature: 240 to 255°CFeed Temperature: 230 to 240°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GGT-1010HF | S&E Specialty Polymers, LLC | PVC+PUR | S&E PVC |
| SLOVAMID® 66 FRC 2 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Monprene® OM-10285-01 | Teknor Apex Company | TPE | Monprene® |
| EvoSource™ ABS 4535 (China) | MBA Polymers | ABS | EvoSource™ |
| LUBAN™ 1104 KTI | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |