Infino GP-5000
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wHDNcK_Infino-GP-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| General PBT material that can be used for connector |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.31 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 74 | g/10 min | ASTM D1238 |
| 250°C/2.16 kg | 71 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.2 to 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 115 | ASTM D785 | |
| R-Scale | 117 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2200 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 55.0 | MPa | ISO 527-2/50 |
| Break 3 | 46.0 | MPa | ASTM D638 |
| Break | 47.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 4.0 | % | ASTM D638 |
| Break | 15 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2300 | MPa | ASTM D790 |
| -- 6 | 2100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 83.0 | MPa | ASTM D790 |
| -- 8 | 74.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 4.9 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 28 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 27 | J/m | ASTM D256 |
| 23°C 10 | 4.5 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 170 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 124 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 75.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 59.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 194 | °C | ISO 306/B50 |
| -- | 185 | °C | ISO 306/B120 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (10 MHz) | 3.10 | ASTM D150 | |
| Dissipation Factor (10 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 140 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.700 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 210 to 220 | °C | |
| Middle Temperature | 225 to 230 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 60.0 to 120 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ad-Tech Polyester NO. 11 TYPE II | Ad-Tech Plastic Systems Corp. | Polyester, TS | Ad-Tech Polyester |
| ExxonMobil™ HDPE HMA 018 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| Duron PA 6,6 33GF-IML | ProPolymers Inc. | Nylon 66 | Duron |
| HiFill FR® PA6 GF13 FR-N BK | Techmer Engineered Solutions | Nylon 6 | HiFill FR® |
| Kaneka MUH BM5600 | Kaneka Corporation | ABS | Kaneka MUH |