Braskem PE ML4400N
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wGzRBG_Braskem-PE-ML4400N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The resin ML4400N is a Linear Low Density Polyethylene developed for rotational molding. It presents high stiffness and an adequate balance of processability and environmental stress cracking resistance. Applications: Water tanks, parts for the automotive and agricultural segments. Processing Conditions: Conditions comparable to polyethylene resins with similar melt index and density range. Oven Temperature Range: 220 to 350 °C. PIAT: 210 a 240°C Additives: Weathering resistance UV8 and antioxidants. conditions comparable to polyethylene resins with similar melt index and density range. Oven Temperature Range: 220 to 350 °C. Additives: Long term UV8 stabilization and antioxidants. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.9 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 2.00mm, 10% Igepal, molded, F50 | 28.0 | hr | ASTM D1693 |
| 50°C, 2.00mm, 100% Igepal, molded, F50 | 300 | hr | ASTM D1693 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 21.0 | MPa | ASTM D638 |
| Fracture, molding | 24.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, molding | 13 | % | ASTM D638 |
| Fracture, molding | > 1000 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Compression Molded) | 670 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength | ARM | ||
| -40°C, 3.17mm, rotational molding | 57 | J | ARM |
| -40°C, 6.34mm, rotational molding | 120 | J | ARM |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, molded | 60.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, molded | 40.0 | °C | ASTM D648 |
| Peak Melting Temperature | 126 | °C | ASTM D3418 |
| Additional Information |
|---|
| Oven Temperature Range: 220 to 350 °C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 30 GFC K1079 LE | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| Sylvin 2925-75 Clear 8392 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Algoflon® L101 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Celanex® 6500HF | Celanese Corporation | PBT | Celanex® |
| Axiall PVC 12770 | Axiall Corporation | PVC, Flexible | Axiall PVC |