ChronoFlex® C 75D
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | CardioTech International, Inc. |
| Trademark: | ChronoFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wGg0ld_ChronoFlex-C-75D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ChronoFlex®C 75D is a polyurethane material,. This product is available in North America and is processed by extrusion. ChronoFlex®The main characteristics of C 75D are: chemical resistance. ChronoFlex®The typical application areas of C 75D are: medical/health care |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 75 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| 100% secant : 23°C | 37.9 | MPa | ASTM D638 |
| 300% secant : 23°C | 20.3 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 290 | % | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.64 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 37.9 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D412 |
| Tensile Elongation (Yield) | 250 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 191 - 221 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Ultimate Tensile Strength, ASTM D638, 73 °F: 7000 to 8000 psiUltimate Tensile Strain, ASTM D638, 73 °F: 255 to 320 %100% Secant Modulus, ASTM D638, 73 °F: 5300 to 5700 psi300% Secant Modulus, ASTM D638, 73 °F: 2700 to 3200 psiAbrasion Resistance, ASTM D1044, 1000 cycles: 0.053%Recommended Sterilization Method, No standard: Ethylene oxideClass VI Biocompactibility Test, USP XXII: Pass |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 216 | °C | |
| Cylinder Zone 2 Temp. | 224 | °C | |
| Cylinder Zone 3 Temp. | 232 | °C | |
| Melt Temperature | 238 | °C | |
| Die Temperature | 238 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205.3A Z | RTP Company | Nylon 6 | RTP |
| Infino CF-1030 | SAMSUNG SDI CO., LTD. | PC | Infino |
| InnoPlus LL7410A | PTT Global Chemical Public Company Limited | LLDPE | InnoPlus |
| LNP™ THERMOCOMP™ EC008 compound | SABIC Innovative Plastics Europe | PEI | LNP™ THERMOCOMP™ |
| Paxon™ AL55-003 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |