SABIC® PPcompound 9156
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wGPedp_SABIC-PPcompound-9156.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 9156 is a mineral filled modified polypropylene. This material combines high scratch resistance, high stiffness, good impact and high flow. This material has a property profile that fullfills Ford Interior requirements. Typical applications include esthetical automotive interior parts such as instrument panels, lower and upper dashboard, door panels and trim. SABIC® PPcompound 9156 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.80 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 20.0 | MPa | |
| Break, Injection Molded | 13.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 1900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 25 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C, Injection Molded) | 25 | kJ/m² | ISO 180/4A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 120 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PP TL203 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Cheng Yu BK1021 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Delrin® 100 BK602 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| ELASTOSIL® E 43 N | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| LG ASA LI931-C | LG Chem Ltd. | ASA | LG ASA |