Zytel® 80G43HS1L BK104
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wFn1ZF_Zytel-80G43HS1L-BK104.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 43% Glass Reinforced, Toughened, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.43 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 4.9 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.5 | -- | % | |
| Viscosity Number | 137 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11700 | -- | MPa | ISO 527-2 |
| Tensile Stress | ||||
| Break | 169 | -- | MPa | ISO 527-2 |
| 23°C | -- | 117 | MPa | ASTM D638 |
| Tensile Elongation | ||||
| Break, 23°C | -- | 4.0 | % | ASTM D638 |
| Break | 3.3 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| 23°C | -- | 6900 | MPa | ASTM D790 |
| -- | 10300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 15 | -- | kJ/m² | |
| 23°C | 23 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 90 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ||||
| 23°C | -- | 270 | J/m | ASTM D256 |
| -40°C | 14 | -- | kJ/m² | ISO 180/1A |
| 23°C | 23 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 78 | -- | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 261 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 1 | 262 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFC8000 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| KumhoSunny PMMA/ABS HAM8541 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Acrylic | KumhoSunny PMMA/ABS |
| MAJORIS ET400 | AD majoris | PP, Unspecified | MAJORIS |
| Sylvin 9915-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| PENTAMID B MK15 E H black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |