LNP™ VERTON™ RV00CEXP compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wFmrL9_LNP-VERTON-RV00CEXP-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV00CE is a compound based on PA 66 resin containing Long Glass Fiber. Added features include; Easy Molding. Also known as: LNP* VERTON* Compound RF-700-12 EM Product reorder name: RV00CEXP |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.71 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.26 | % | |
| Across Flow | 0.61 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 21600 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 270 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 19000 | MPa | ISO 178 |
| Flexural Stress | 430 | MPa | ISO 178 |
| Flexural Strain at Break 2 | 2.6 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -40°C | 43 | kJ/m² | |
| 23°C | 53 | kJ/m² | |
| Unnotched Izod Impact Strength 4(23°C) | 100 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 255 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 252 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.7E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purgex™ 457 Plus | Neutrex, Inc. | PE, Unspecified | Purgex™ |
| Sanren M700R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| TEREZ PA 6 7100 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Bergamid™ B700 G25 H | PolyOne Corporation | Nylon 6 | Bergamid™ |
| BMC 1901 | Bulk Molding Compounds, Inc. | Alkyd | BMC |