Sindustris POM FW721F
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wFQHfb_Sindustris-POM-FW721F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris POM FW721F is an Acetal (POM) Homopolymer material. It is available in Asia Pacific for injection molding. Important attributes of Sindustris POM FW721F are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 to 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 78.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 110 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | ||
| 3.00 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 160 to 180 | °C | |
| Middle Temperature | 170 to 190 | °C | |
| Front Temperature | 180 to 200 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Back Pressure | 0.490 to 3.04 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PS High Impact IS200 | M. Holland Company | PS (HIPS) | MTEGRITY™ PS High Impact |
| Vipel® F701-FBG-20 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| ULTRATUF™ SG | Spartech Plastics | PC | ULTRATUF™ |
| Gallonprene® GP210-6009 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| OnFlex™ S EH 80A-3S7005 | PolyOne Corporation | TPE | OnFlex™ |