Infino EF-1032
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wEmxqY_Infino-EF-1032.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion resin of non-halogen flame-retardant characteristic |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 20 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2300 | MPa | ASTM D638 |
| -- | 2400 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break 3 | 69.0 | MPa | ASTM D638 |
| Break | 55.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 120 | % | ASTM D638 |
| Break | 73 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2400 | MPa | ASTM D790 |
| -- 6 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 93.0 | MPa | ASTM D790 |
| -- 8 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 62 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 830 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 420 | J/m | ASTM D256 |
| 23°C 10 | 53 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 103 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 92.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ISO 306/B50 |
| -- | 129 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.00 mm | 5VB | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90.0 | °C | |
| Desiccant Dryer | 90.0 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Pressure | 98.1 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® H110MA | Reliance Industries Limited | PP Homopolymer | REPOL® |
| GELAST 5160A | Guang Sung Plastics (GSPL) | ABS | GELAST |
| Grilon® TSGL-50-4 nat | EMS-GRIVORY | Nylon 66/6 | Grilon® |
| POLYfill PP CV8030 LR | Polykemi AB | PP, Unspecified | POLYfill |
| Mediprene® 880135 | ELASTO | SEBS | Mediprene® |