TECHNYL® A 20 V35 BLACK 25
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wDzG1l_TECHNYL-A-20-V35-BLACK-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant polyamide 66, reinforced with 35% of glass fibre, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.60 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 10000 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield | 190 | 140 | MPa | |
| Break | 170 | 140 | MPa | |
| Tensile Strain | ISO 527-2/1A | |||
| Yield | 2.0 | 3.0 | % | |
| Break | 2.0 | 3.0 | % | |
| Flexural Modulus | 10000 | 7500 | MPa | ISO 178 |
| Flexural Stress | 260 | 200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 10 | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 65 | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 10 | 12 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 25 | 25 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.050 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 400 | 375 | V | |
| Solution B | 325 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| Glow Wire Flammability Index (1.60 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 275 to 280 | °C | |
| Middle Temperature | 285 to 290 | °C | |
| Front Temperature | 290 to 295 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL NY6-M40- (color)H | Polymer Resources Ltd. | Nylon 6 | PRL |
| RTP EMI 161 Z | RTP Company | PP, Unspecified | RTP |
| LIHAN® B9000N | Nanjing Lihan Chemical Co., Ltd. | Nylon 6 | LIHAN® |
| LNP™ THERMOCOMP™ RC003SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |
| AKROLEN® PP GFM 25/15 natural (2118) | AKRO-PLASTIC GmbH | PP, Unspecified | AKROLEN® |