Sicoflex S299
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Ravago Group |
| Trademark: | Sicoflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wDpQho_Sicoflex-S299.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ABS 17% glass fibre filled heat resistant grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 3.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.30 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -23°C | 3.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 118 | °C | ISO 306/A50 |
| -- | 107 | °C | ISO 306/B50 |
| Ball Pressure Test (75°C) | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 575 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 28 | mm/min | FMVSS 302 |
| Flame Rating 1 | Internal Method | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | UL94 internally tested |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 662 | RTP Company | ABS | RTP |
| Tarnoform® 300 EC2 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| VITAMIDE® AS30VN6457 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Mylar® MO 21 (900 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| EPO-TEK® H20E-PFC | Epoxy Technology Inc. | Epoxy | EPO-TEK® |