CYCOLOY™ LG9000 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wDn9xr_CYCOLOYLG9000resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CYCOLOY LG9000 is a low gloss PC+ABS injection moulding grade. LG9000 combines good impact / heat and UV resistance with a low gloss surface appearence. It is suitable for automotive interior applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ISO 2039-2 | |
| Ball Indentation Hardness (H 358/30) | 93.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 50.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Fracture | 40.0 | MPa | ISO 527-2/5 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/5, ISO 527-2/50 | ||
| Yield | 4.0 | % | ISO 527-2/5, ISO 527-2/50 |
| Fracture | 10 | % | ISO 527-2/5, ISO 527-2/50 |
| Flexural Modulus 2 | 2400 | MPa | ISO 178 |
| Flexural Stress | 81.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 82.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 20 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 20 | kJ/m² | ISO 180/1A |
| 23°C | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 100 mm span | 120 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 97.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 122 | °C | ISO 306/B50 |
| -- | 124 | °C | ISO 306/B120 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 75°C | Pass | IEC 60695-10-2 | |
| 110°C 6 | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 0.800mm, in oil | 35 | kV/mm | IEC 60243-1 |
| 1.60mm, in oil | 25 | kV/mm | IEC 60243-1 |
| 3.20mm, in oil | 17 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 50 Hz | 2.60 | IEC 60250 | |
| 60 Hz | 2.60 | IEC 60250 | |
| 1 MHz | 2.60 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 50 Hz | 1.0E-3 | IEC 60250 | |
| 60 Hz | 1.0E-3 | IEC 60250 | |
| 1 MHz | 9.0E-3 | IEC 60250 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| Comparative Tracking Index | 275 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (1.00 mm) | 35 | mm/min | ISO 3795 |
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 95.0 - 105 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 220 - 250 | °C | |
| Middle Temperature | 240 - 280 | °C | |
| Front Temperature | 240 - 280 | °C | |
| Nozzle Temperature | 230 - 270 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 |
| 5 . | 120*10*4 mm |
| 6 . | Approximate maximum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| QR Resin QR-4100-GF20 | QTR, Inc. | PPE+PS | QR Resin |
| UNILATE® PBT | Nytef Plastics, Ltd. | PBT | UNILATE® |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYfill PPC BGK601213 CR | Polykemi AB | PP Copolymer | POLYfill |
| LEXAN™ 923X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |