Order Products : sales@su-jiao.com
Generic EAA
| Category: | EAA , Ethylene Acrylic Acid Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wDgGg4_Generic-EAA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EAA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.930 - 0.940 | g/cm³ | ASTM D792 |
| 23°C | 0.930 - 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.80 - 33 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 1.3 - 34 | g/10 min | ISO 1133 |
| Acrylic Acid Content | 6.0 - 11.2 | wt% | |
| Comonomer Content | 6.1 - 10.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 25 - 80 | ASTM D2240 | |
| 23°C | 38 - 51 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 7.00 - 10.0 | MPa | ASTM D638 |
| Yield, 23°C | 5.00 - 9.50 | MPa | ISO 527-2 |
| Fracture, 23°C | 4.91 - 26.1 | MPa | ASTM D638 |
| Fracture, 23°C | 5.60 - 23.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 410 - 750 | % | ASTM D638 |
| Fracture, 23°C | 590 - 650 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 20.0 - 113 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 40.0 - 88.9 | °C | ASTM D1525 |
| -- | 40.0 - 90.0 | °C | ISO 306 |
| Melting Temperature (DSC) | 95.8 - 101 | °C | ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 135 - 185 | °C | |
| Cylinder Zone 2 Temp. | 160 - 235 | °C | |
| Cylinder Zone 3 Temp. | 185 - 260 | °C | |
| Cylinder Zone 4 Temp. | 185 - 285 | °C | |
| Cylinder Zone 5 Temp. | 185 - 285 | °C | |
| Adapter Temperature | 185 - 285 | °C | |
| Melt Temperature | 260 - 312 | °C | |
| Die Temperature | 185 - 285 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic EAAThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propilven J-400 | Propilven, S.A. | PP, Unspecified | Propilven |
| Sylvin 9610-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| APEX® 82-E322B-NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Elastron® G P.G401.A90.N | Elastron USA, Inc. | SEBS | Elastron® G |
| KOPLA PA66 KDU1021 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |