TPX® MX004
| Category: | PMP Copolymer , Polymethylpentene Copolymer |
| Manufacturer: | Mitsui Chemicals America, Inc. |
| Trademark: | TPX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wCU39d_TPXMX004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TPX®MX004 is a polymethylpentene copolymer (PMP copolymer) material,. This product is available in Europe or Asia Pacific region. The processing method is extrusion or injection molding. TPX®The main characteristics of MX004 are: hardness. TPX®Typical application areas of MX004 are: food contact applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.834 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.9 | % | ASTM D955 |
| Transverse flow | 1.7 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 73 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1180 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 23°C | 25.0 | MPa | ASTM D638 |
| 23°C | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 48 | % | ASTM D638 |
| Flexural Modulus (23°C) | 980 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 33.8 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 170 | °C | ASTM D1525 |
| Melting Temperature | 227 | °C | |
| CLTE - Flow | 3.8E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 63 | kV/mm | ASTM D149 |
| Dielectric Constant | 2.12 | ASTM D150 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.463 | ASTM D542 | |
| Clarity | 94.0 | ASTM D1746 | |
| Haze | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| Unnotched Izod Impact, ASTM D256, 23°C: 98 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4215 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| NYCOA Polyamide 4230 HST | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| BITONER® C9 BP-120 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| Bormod™ BE961MO | Borealis AG | PP Copolymer | Bormod™ |
| DENYL HT 3510 Y | Vamp Tech | PPA | DENYL |