Witcom PA66 6G/3L3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PA66 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | wBphxZ_Witcom-PA66-6G-3L3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PA66 6G/3L3 is a polyamide 66 (nylon 66) product, which contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.47 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.35 - 0.50 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 4.7 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.4 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 - 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 225 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 70 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 275 - 295 | °C | |
| Mold Temperature | 60.0 - 95.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 to 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2605 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Sanren F200A (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| ResMart Ultra CoPP 20-NB | ResMart | PP Impact Copolymer | ResMart Ultra |
| Starex LX-0970 LS | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Elastron® G G300.A55.N | Elastron USA, Inc. | SEBS | Elastron® G |