Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	Eltex® P
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	wBIODT_EltexPKS407HP.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Polypropylene - Heat Seal Benefits & Features Eltex® P KS407HP is a modified random copolymer with a high ethylene content, developed for use primarily as the sealing layer in "coextruded bioriented metallisable film". It contains no technical additives and is thus particularly appreciated by users wishing to use their own "formulas". Its stabilisation package has been especially designed for metallisable film applications. Good metal adhesion Good processability on high speed BOPP lines Longer Corona surface treatment retention Applications Sealing layers for further converting operations (metallisation, lamination, printing).

Message

Polypropylene - Heat Seal

Benefits & Features
Eltex® P KS407HP is a modified random copolymer with a high ethylene content, developed for use primarily as the sealing layer in "coextruded bioriented metallisable film". It contains no technical additives and is thus particularly appreciated by users wishing to use their own "formulas". Its stabilisation package has been especially designed for metallisable film applications.

Good metal adhesion

Good processability on high speed BOPP lines

Longer Corona surface treatment retention

Applications
Sealing layers for further converting operations (metallisation, lamination, printing).

General Information
Features	Electroplating Workability, good Good adhesion Random copolymer No additive
Uses	Bi-axially Oriented Film Films
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Bi-axially Oriented Film Co-extrusion molding

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	5.0	g/10 min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus (23°C)	720	MPa	ISO 178

Films	Nominal Value	Unit	Test Method
Heat seal threshold ¹	115	°C	Internal method

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	134	°C	ASTM D3417

Note Message
1 .	1s, 3 bars, 100 mm/min, 100 g/cm

Resin Grade	Manufacturer	Category	Trademark
TAISOX 6630M	Formosa Plastics Corporation	LDPE	TAISOX
Tufpet PBT FEX70	Mitsubishi Rayon America Inc.	PBT	Tufpet
Ultraform® N 2310 P Q600	BASF Corporation	Acetal (POM) Copolymer	Ultraform®
Haysite Plastics H722	Haysite Reinforced Plastics	Polyester, TS	Haysite Plastics
PARAPET GR04940	Kuraray Co., Ltd.	Acrylic (PMMA)	PARAPET