Order Products : sales@su-jiao.com
Zytel® ST811HS BK038
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w9fWvh_ZytelST811HSBK038.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super Toughened, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 0.90 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 900 | 400 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 31.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 29 | -- | % | ISO 527-2 |
| Flexural Modulus | 850 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 12 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 80 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | -- | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -40°C | 13 | -- | kJ/m² | ISO 180/1A |
| 23°C | 65 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | No Break | -- | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 85.0 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 50.0 | 0.00 | °C | ISO 11357-2 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.3E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.4E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 4.00 | s/mm | |
| Maximum Screw Tangential Speed | 300 | mm/sec |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Extrusion Melt Temperature, Optimum | 240 | °C |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Ejection Temperature | 190 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 60 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.060 | % | |
| Melt Temperature | 235 - 250 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA/ABS Blend 2010/2 | TER HELL PLASTIC GMBH | ABS+Nylon | TEREZ PA/ABS |
| Ducor® DE1040V | Ducor Petrochemicals BV | PP Homopolymer | Ducor® |
| KPOL-LDPE LD K-1.40/920 | KPOL Chem Co. | LDPE | KPOL-LDPE |
| POLYabs P0P | Polykemi AB | ABS | POLYabs |
| ESTOPLAST XU 150GY67 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |