RTP 207A TFE 15 HS
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w9Sqpr_RTP-207A-TFE-15-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 159 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 8960 | MPa | ASTM D790 |
| Flexural Strength | 234 | MPa | ASTM D790 |
| Compressive Strength | 138 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (6.35 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 210 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| CLTE - Flow | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.52 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D-955, 0.25in.: 3mil/in.Tensile Elongation, ASTM D-638: 2-3%Flammability, ASTM D-635: B in/min. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 260 | °C | |
| Middle Temperature | 232 - 260 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SBS 1003 | Network Polymers, Inc. | SBS | Network Polymers SBS |
| ASI POLYPROPYLENE PP 2407-01 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Fiberfil® J-60/40/E8 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| LubriOne™ PC-000/5T-2S BK002 | PolyOne Corporation | PC | LubriOne™ |
| Sylvin 4280-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |