GUR® GHR 8020
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Celanese Corporation |
| Trademark: | GUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w9GsIN_GUR-GHR-8020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GHR 8020 is a linear polyolefin in powder form with a molecular weight of approximately 300,000 g/mol calculated using Margolies' equation and a coarse particle size. It is mainly used for production of porous products. The average particle size is d50 = 210 ¦ 20 ¦m. The bulk density is approx. 0.45 g/cm3. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 19.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 10 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/1A/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525 |
| Melting Temperature 1 | 133 | °C | ISO 11357-3 |
| CLTE - Flow | 2.0E-4 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1840 | J/kg/°C | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4099 X 113516 A | RTP Company | PPA | RTP |
| Toraypef® 30030 AP17 | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| Electrafil® TPU/E 06001 | Techmer Engineered Solutions | TPU-Polyether | Electrafil® |
| ESTACARB 2060 V0 HF | Cossa Polimeri S.r.l. | PC | ESTACARB |
| Karina CLEAR PVC COMPOUND 75/208-D-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |