POLYLAC® PA-747F
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8zRA2_POLYLAC-PA-747F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-747F is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| 23°C | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 0.30 | g/10 min | |
| 220°C/10.0 kg | 3.0 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 3.30 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 99.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 46.0 | MPa | ISO 527-2/50 |
| Break | 35.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 47.6 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 35 | % | ASTM D638 |
| Break | 20 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 2550 | MPa | ASTM D790 |
| -- 4 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 71.6 | MPa | ASTM D790 |
| -- 6 | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 27 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 310 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 250 | J/m | ASTM D256 |
| -- | 25 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 89.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 95.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 106 | °C | ASTM D1525, ISO 306/A50 6 7 |
| -- | 101 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 190 to 210 | °C | |
| Cylinder Zone 3 Temp. | 210 to 240 | °C | |
| Cylinder Zone 5 Temp. | 220 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ OM 6275-1 | PolyOne Corporation | TPE | Versaflex™ |
| TUFNYL® SST 20 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Niretan B S25 AE/V0 | Soredi S.p.a. | Nylon 6 | Niretan B |
| Bamtac BPP035A | Ningbo Bamtac New Material Col, Ltd. | PP, Unspecified | Bamtac |
| ASTALON™ S2000U | Marplex Australia Pty. Ltd. | PC | ASTALON™ |