KOPLA PA6 KNE1010
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8ua8s_KOPLA-PA6-KNE1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KNE1010 is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific. Important attributes of KOPLA PA6 KNE1010 are:
Typical application of KOPLA PA6 KNE1010: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.8 to 2.4 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.4 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | > 200 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1860 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 390 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 165 | °C | |
| 1.8 MPa, Unannealed | 55.0 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.80 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Q30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Ultradur® B 2550 | BASF Corporation | PBT | Ultradur® |
| INELEC PCCF30 | Infinity LTL Engineered Compounds | PC | INELEC |
| Idemitsu PS NS-251 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| ULTEM™ HU1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |