Escorene™ Ultra FL 00218
| Category: | EVA , Ethylene Vinyl Acetate Copolymer Resin |
| Manufacturer: | ExxonMobil Chemical |
| Trademark: | Escorene™ Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8PTbO_Escorene-Ultra-FL-00218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FL 00218 is a copolymer of ethylene and vinyl acetate with low crystal point. When the processing temperature is higher than 240 C (464 °F) in processing conditions, resin degradation may be caused. The machine should be thoroughly cleaned with low density polyethylene or suitable detergent before stopping. |
| General Information | |
|---|---|
| Additive |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.7 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% | ExxonMobil Method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD | 48.0 | MPa | ASTM D882 |
| 1% secant, TD | 50.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Fracture | 37.0 | MPa | ASTM D882 |
| TD : Fracture | 36.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 550 | % | ASTM D882 |
| TD : Fracture | 720 | % | ASTM D882 |
| Dart Drop Impact | 660 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 70 | g | ASTM D1922 |
| TD | 170 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 62.0 | °C | ASTM D1525 |
| Legal statement |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 H AR 5 TFE 10 | RTP Company | Nylon 66 | RTP |
| SCANTEC PC S60R GF20 V0 | Polykemi AB | PC | SCANTEC |
| Sinelec CCB6825 | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| NAXELL™ PC110VL | MRC Polymers, Inc. | PC | NAXELL™ |
| POLYLAC® PA-757GJ08 | CHI MEI CORPORATION | ABS | POLYLAC® |