Ebalta AH 140 / LI 60
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w8CF1O_Ebalta-AH-140-LI-60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Opened containers should be rapidely consumed, the hardener LI 60 tends to change in colour becoming brownish in contact with oxygen. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 to 87 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 2750 to 3250 | MPa | ISO 178 |
| Flexural Stress | 110 to 130 | MPa | ISO 178 |
| Compressive Stress | 80.0 to 90.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 to 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 102 to 108 | °C | ISO 75-2/B |
| Glass Transition Temperature | 95.0 | °C | DSC |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 35 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time | |||
| 60°C | 4.0 | hr | |
| 80°C | 6.0 | hr | |
| 120°C | 4.0 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.10 to 1.14 | g/cm³ | |
| Viscosity (25°C) | 0.53 to 0.68 | Pa·s | |
| Curing Time (20°C) | 20 to 24 | hr | |
| Pot Life 1(20°C) | 50 to 60 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sekisui PVC TG-H500 | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| Elastron® V V101.D35.B | Elastron USA, Inc. | TPV | Elastron® V |
| LNP™ COLORCOMP™ DX13304C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| Axiall PVC 7465A | Axiall Corporation | PVC, Rigid | Axiall PVC |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |