LNP™ THERMOCOMP™ LX08411 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w7OyyM_LNP-THERMOCOMP-LX08411-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP LX08411 is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added feature of this material is: Opaque. Also known as: LNP* THERMOCOMP* Compound LX08411 Product reorder name: LX08411 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.28 | % | |
| Across Flow : 24 hr | 0.75 to 0.85 | % | |
| Water Absorption (24 hr, 50% RH) | 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 23500 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 270 | MPa | |
| Break | 270 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 1.8 | % | |
| Break | 1.8 | % | |
| Flexural Modulus 4(50.0 mm Span) | 25000 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0 mm Span | 366 | MPa | |
| Break, 50.0 mm Span | 366 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 70 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 780 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 341 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 327 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 370 to 380 | °C | |
| Middle Temperature | 380 to 400 | °C | |
| Front Temperature | 380 to 400 | °C | |
| Mold Temperature | 175 to 190 | °C | |
| Back Pressure | 0.300 to 0.700 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SITRAMID CF10-M15 / C94150 | SITRAPLAS GmbH | Nylon 6 | SITRAMID |
| Sylvin 8240-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Edgetek™ AT-000/000 HI 10 Natural | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| ELIX™ Ultra 4115 | ELIX Polymers, S. L. | PC+ABS | ELIX™ Ultra |
| PLEXIGLAS® Sheet XT, UV transmitting Clear 0A770 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |