HAIPLEN H30 K6 BA X0
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | HAIPLEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w74F4F_HAIPLEN-H30-K6-BA-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer 30% glass beads reinforced chemical coupled self extinguishing V0. UL94 V0 - all colors - 1,5 mm Available: all colors, UV stabilized (L), heat stabilized (H), laser printable (LP), detergent stabilized(D). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 to 0.35 | % | |
| Across Flow | 0.25 to 0.35 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.050 | % | ASTM D570, ISO 62 |
| Saturation | 0.15 | % | ASTM D570 |
| Saturation, 23°C | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 40.0 | MPa | ISO 178 |
| Yield | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A 4 2 |
| -- | 125 | °C | ASTM D1525, ISO 306/B 5 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (3.20 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 27 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Loading 1 (10 N) |
| 3 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VESTAMID® L L2106F | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| Casico™ FR4807 | Borealis AG | Polyolefin, Unspecified | Casico™ |
| Kepital® MF3025 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| POLIMAXX 422F | IRPC Public Company Limited | PS (EPS) | POLIMAXX |
| Infino NH-1000T | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |