Bakelite® PF 7595
| Category: | Phenolic , Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w6Zas6_Bakelite-PF-7595.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Phenolic moulding compound, inorganically/organically filled, modified with graphite, good heat conductivity, good sliding properties, conductive in electrical properties Application Areas Bearers for grinding disc centers, gas meter parts, pump parts, sliding/guiding elements, glide bearing parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.59 | g/cm³ | ISO 1183 |
| Apparent Density | 0.85 | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.20 | % | |
| -- 2 | 0.25 | % | |
| Water Absorption - 24h/23C | 6.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 3 | 0.10 | % | |
| -- 4 | 0.10 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 440 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress | 45.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 12000 | MPa | ISO 178 |
| Flexural Stress 5 | 80.0 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 170 | °C | ISO 75-2/C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Compression |
| 2 . | Injection |
| 3 . | Injection |
| 4 . | Compression |
| 5 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4095 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sanren Y600 (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TEKAPPO™ J930 | Mando Advanced Materials Co., Ltd. | PPE+PS | TEKAPPO™ |
| DOW™ HDPE DMDA-8904 HEALTH+™ | The Dow Chemical Company | HDPE | DOW™ HDPE |
| DOW™ LDPE 310E | The Dow Chemical Company | LDPE | DOW™ LDPE |