LNP™ LUBRICOMP™ OCL36 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w5ggLv_LNP-LUBRICOMP-OCL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* OCL36 is a compound based on PPS - Linear resin containing 30% Carbon Fiber, 15% PTFE. Added features of this material include: Electrically Conductive, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound OCL-4036 Product reorder name: OCL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.040 to 0.10 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.36 to 0.40 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.031 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 21500 | MPa | ASTM D638 |
| -- | 30700 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 169 | MPa | ASTM D638 |
| Break | 167 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.4 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 21100 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | |||
| -- | 259 | MPa | ASTM D790 |
| -- | 262 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.34 | ||
| Wear Factor - Washer | 19.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 6.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 31 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.1 | J | ASTM D3763 |
| -- | 2.97 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 267 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 263 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 3.4E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.80 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Amilan® CM8000 | Toray Resin Company | Nylon Copolymer | Amilan® |
| Dartek O-401 | DuPont Canada, Inc. - Dartek Division | Nylon 66 | Dartek |
| Leostomer® ER2084 | Riken Technos Corp. | SBC | Leostomer® |
| LUVOCOM® 80-8003 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Sylvin 916VO-95C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |