Fibremod™ GD301FE
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Fibremod™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w4khhI_Fibremod-GD301FE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibremod GD301FE is a 30 % chemically coupled high Performance glass fibre reinforced polypropylene compound intended for injection moulding. This material shows excellent mechanical properties also at elevated temperatures. The product is available in standard black 9502. Applications : Fibremod GD301FE has been developed especially for applications like:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | Internal method | ||
| Vertical flow direction : 2.00mm | 0.90 | % | Internal method |
| Flow direction : 2.00mm | 0.15 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 6500 | MPa | ISO 178 |
| Flexural Stress | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 54 | kJ/m² | ISO 179/1eU |
| 23°C | 59 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 9.5 | kJ/m² | ISO 180/1A |
| 23°C | 11 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 158 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 148 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 139 | °C | ASTM D1525 3 |
| Melt Energy | 67.2 | kJ/kg | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 16 hr (100°C) | 1.0 | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | 40.0 | µgC/g | VDA 277 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 3.00 - 6.00 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 to 80°CBack Pressure: As low as possibleScrew Speed: Low to MediumFlow Front Speed: 100 to 200 m/min |
| Note Message | |
|---|---|
| 1 . | 150x80x2 mm |
| 2 . | 2.0 mm/min |
| 3 . | 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM ABS 7520 | Ponachem Compound GmbH | ABS | PONACOM ABS |
| RTP 209 MS | RTP Company | Nylon 66 | RTP |
| SILVER® SA-2302 | Guangdong Silver Age Sci & Tech. Co., Ltd | SEBS | SILVER® |
| APEX® 94-A0098C-60 | Teknor Apex Company | PVC, Flexible | APEX® |
| DJSilicone NE-9270 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |