Sicoklar E01.04
| Category: | PC , Polycarbonate |
| Manufacturer: | Ravago Group |
| Trademark: | Sicoklar |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w3yXbw_Sicoklar-E01-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC, extrusion grade |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 65.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Strain (Break) | 70 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 20 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 144 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm, in Oil) | 17 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | Internal Method | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| 0.750 mm | V-2 | ||
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | UL94 internally tested |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP6443 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| VECTRA® E840i LDS | Celanese Corporation | LCP | VECTRA® |
| KF 1100 | Kureha Corporation | PVDF | KF |
| Osterlene® PPC-.75-NB | Osterman & Company | PP Impact Copolymer | Osterlene® |
| Polene EVA SV1055 | TPI Polene Public Company Limited | EVA | Polene EVA |