Andur 9200 AP/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w2e8rY_Andur-9200-AP-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 9200-AP is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 92 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 9200-AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 93 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 0.545 | MPa | ASTM D695 |
| 10% strain | 2.48 | MPa | ASTM D695 |
| 15% strain | 4.41 | MPa | ASTM D695 |
| 25% strain | 6.18 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 9.65 | MPa | ASTM D412 |
| 300% strain | 22.8 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 340 | % | ASTM D412 |
| Compression Set | 30 | % | ASTM D395B |
| Bayshore Resilience | 30 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 2.5 - 4.5 | min | |
| Demold Time | 30 - 45 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 91 to 94Die C Tear, ASTM D1004: 375 pliAverage Split Tear, ASTM D1938: 115 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 9200 AP: 180-212°F Curene 442: 235-250°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 104 - 113 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NILENE® E6 K20VA V0 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Next Nylon 66 Prime Series PXH-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ACCUCOMP™ ABS892EL | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| Karina BLACK PVC COMPOUND -E 806D48/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ IX04513C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |