STRATOR® C-4
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | EPIC Polymers |
| Trademark: | Strator® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w2XtGf_STRATOR-C-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STRATOR®C- 4 is a thermoplastic product that contains 40% long glass fibers as filler. It is available in Europe. The main characteristics are: high strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| -- | -- | 11000 | MPa | ISO 527-2 |
| 23°C | 13000 | -- | MPa | ISO 527-2 |
| 90°C | 8800 | -- | MPa | ISO 527-2 |
| 120°C | 7800 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Fracture, 23°C | 220 | 190 | MPa | ISO 527-2 |
| Fracture, 90°C | 145 | -- | MPa | ISO 527-2 |
| Fracture, 120°C | 125 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10900 | -- | MPa | ISO 178 |
| Flexural Stress (23°C) | 330 | 270 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | 35 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 70 | 90 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 237 | -- | °C | ISO 75-2/A |
| CLTE - Flow | 2.3E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.33 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 270 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Nozzle Temperature | 285 - 320 | °C | |
| Processing (Melt) Temp | < 310 | °C | |
| Mold Temperature | 80.0 - 160 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 377 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| Sylvin 8813-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ELITE™ 5110G | The Dow Chemical Company | EPE | ELITE™ |
| GPP™ 1001V0F | S&E Specialty Polymers, LLC | TPO (POE) | GPP™ |
| Rotuba CAP CP801 (16% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |