DOW™ HDPE TCP-2495 NT
| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w12hC4_DOW-HDPE-TCP-2495-NT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Comply with industry standards
DOW TCP-2495 NT high density polyethylene resin is prepared by UNIPOL™Processing technology. This product is specially used for processing all conduits and cables of CIC circuits, and is used in telecommunication and power cable applications. After blending the primary color resin with the color masterbatch, it can be processed in the existing pipe or pipeline extrusion process, and is suitable for all sizes. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.946 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.21 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 21 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance 1(F0) | > 3000 | hr | ASTM D1693C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 22.8 | MPa | ASTM D638 |
| Fracture | 34.5 | MPa | ASTM D638 |
| Tensile Elongation 4(Break) | > 1000 | % | ASTM D638 |
| Flexural Modulus | 862 | MPa | ASTM D790B |
| Slow crack propagation PENT 5(80°C) | > 10 | hr | ASTM F1473 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6(23°C) | 110 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature 7 | < -95.0 | °C | ASTM D746A |
| Melting Temperature (DSC) | 128 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 227 | °C |
| Extrusion instructions |
|---|
| 挤塑管的制造条件： 螺杆类型：高质量 HDPE（对于完全熔解最好使用阻隔） 熔体温度范围：400-440 °F (205-225 °C) |
| Note Message | |
|---|---|
| 1 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| 2 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| 3 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| 4 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| 5 . | 2.4 MPa |
| 6 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| 7 . | Prepare the compression molded fittings according to procedure C. Attributes will vary with molding conditions and aging time. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120ST | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Nanjing Hongrui PA6 B353 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| Grilon® CR 9 | EMS-GRIVORY | Nylon 6/12 | Grilon® |
| Karina BLACK COLOR CONCENTRATE 48/1-FC-6 (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Eltex® PF6812AA | INEOS Olefins & Polymers Europe | mLLDPE | Eltex® |