Koattro KT AR05
| Category: | Plastomer , Ethylene-based Plastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Koattro |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | w0QiiO_Koattro-KT-AR05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Koattro KT AR05 is a novel plastomeric material based on LyondellBasell technology with unique characteristics. The product shows an excellent compression set performance which is highly compatible with Polypropylene. Blended with PP it enhances softness, elastic recovery, elongation at break and impact resistance whilst improving transparancy and reducing stress whitening. Blended at low concentrations in PP, Koattro KT AR05 enhances also the thermal bonding strength. KT AR05 is available in free flowing pellet form. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 87 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19.0 | MPa | ISO 527-2 |
| Tensile Stress (Break, Compression Molded) | 12.0 | MPa | ISO 8986-2 |
| Tensile Strain (Break, Compression Molded) | > 400 | % | ISO 8986-2 |
| Flexural Modulus (23°C) | 25.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compression Set (70°C) | 42 | % | ASTM D395B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 5.1 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 114 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polystyrene Crystal 1960N | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |
| U-polymer AXF-1500-05 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| ACRYPET® IR H30 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Algoflon® F 7 | Solvay Specialty Polymers | PTFE | Algoflon® |
| Kingfa PP-V10 | Kingfa | PP, Unspecified | Kingfa |