TABOREX TA 1108 HD
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | SILON s.ro |
| Trademark: | TABOREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vzpzkB_TABOREX-TA-1108-HD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
A chemically-crosslinkable HDPE compound for the production of pipes for domestic hot and cold water, under floor heating and central heating application. TA 1108 HD is a crosslinkable compound made by Silane grafted ethylene polymer. This graft polymer constitutes together with a Masterbatch containing the crosslinking catalyst a "SIOPLAS-SYSTEM". Pipes produced with the SILON grade TA 1108 HD fulfil the requirements of ASTM F876-99a, ASTM F877-99a, CSA 137.5-99, DIN 16892 and all related standards. This system allows the compound to be extruded as a normal thermoplastic polymer, which will attain a high level of crosslinking in the processed form. The final product has all the improved properties associated with crosslinked polyethylene. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.942 | g/cm³ | DIN 53479, ASTM D1505 |
| Apparent Density | 0.53 | g/cm³ | DIN 53466 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 2.3 | g/10 min | Internal method |
| Moisture Content | % | Internal method | |
| Volatile Matter | % | Internal method | |
| Gel Content 1 | 75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 250 | % | ISO 527-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 160 - 170 | °C | |
| Cylinder Zone 2 Temp. | 170 - 180 | °C | |
| Cylinder Zone 3 Temp. | 170 - 190 | °C | |
| Cylinder Zone 4 Temp. | 170 - 190 | °C | |
| Die Temperature | 190 - 220 | °C |
| Extrusion instructions |
|---|
| L/D: >25Compression ratio: 3:1 to 2.5 : 1Head: 200 to 210°CScrew: 70°C to 90 °C |
| Note Message | |
|---|---|
| 1 . | DIN 16892/ ASTM F 876-99a |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PQ 83 T 40 | Plastcom | PP+EPDM | SLOVALEN® |
| TPUCO® TPUI-T64D | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Jampilen HP562S | Jam Polypropylene Company | PP Homopolymer | Jampilen |
| Pearlthane® 91T85 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® |
| Badatech HT® PEEK 3111 GF 30 | Bada AG | PEEK | Badatech HT® |