Nylfor® R 66 CM/17 E9 L5 UV BLACK FXT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Nylfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vzl3CM_Nylfor-R-66-CM-17-E9-L5-UV-BLACK-FXT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, 17% mineral filled, impact modified, UV and heat stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 55.0 | MPa | |
| Break | 50.0 | MPa | |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Stress | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 60 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-270 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Loyblend® TA-1000 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |
| LubriOne™ NN-10GF/10T BLACK | PolyOne Corporation | Nylon 66 | LubriOne™ |
| POFEX EP8300S 70DM | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |
| Optix® CP-1000 IG | Plaskolite, Inc. | Acrylic (PMMA) | Optix® |