SABIC® Vestolen A RELY 5924R 10000 is a grade which has a high density and a bimodal distribution of the molecular mass. Due to the low sag characteristics of this material it may be used for the production of thick walled (large diameter and low SDR) pipes for infrastructure and industrial applications and shows favorable processing behaviour. This material meets (inter)national standards for use in gas, drinking water and waste water piping. MRS class ISO 12162 MPa = 10.0 (PE 100). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | < 0.10 | g/10 min | |
| 190°C/5.0 kg | 0.23 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.00 mm, Compression Molded) | 1000 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress (Yield, 2.00 mm, Compression Molded) | 24.0 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain (Yield, 2.00 mm, Compression Molded) | 8.0 | % | ISO 527-2/1BA/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Compression Molded | 9.0 | kJ/m² | |
| 23°C, Compression Molded | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 72.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 44.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 74.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 124 to 128 | °C | DIN 53765 |
| Oxidation Induction Time - Compression Molded (210°C) | > 20 | min | ISO 11357-6 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MRS Classification | 10.0 | MPa | ISO 12162 |
| RAL Number | 9004 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wellamid® GFT13-66 XE-NBK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ultralloy™ 108 White | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| ACCUTECH™ HP0339T30L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Andur 6500 DPLF/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Boltaron Rigiwall® 4343/4353 | Boltaron Performance Products | PMMA+PVC | Boltaron |